Fluorocarbonorecubrimientos
KF-FEVE500 Fluorocarbon Coating
Kexin KF-FEVE500 fluorocarbon coating uses trifluorochloroethylene-vinyl ether (FEVE) copolymer resin and a highly weather-resistant pigment system. With a C-F bond energy of up to 485 kJ/mol (far exceeding ultraviolet light energy), the coating provides outstanding outdoor weather resistance for over 25 years. It is the preferred top-tier protective finish for landmark buildings and major projects such as architectural aluminum curtain walls, metal roof panels, and large steel structures. The coating also offers comprehensive excellent properties including self-cleaning, stain resistance, resistance to strong acids and alkalis, and salt spray resistance.
ProductsDescripción general
Fluorocarbon coating is a high-performance professional coating product developed and produced by Kexin New Materials. It is scientifically formulated with high-quality resin and imported pigments and fillers, offering excellent adhesion, durability, and application performance. It is widely used in industrial manufacturing, architectural decoration, automotive transportation, and other fields.
As a source coating factory, Kexin New Materials strictly adheres to the ISO9001 quality management system in the formulation design, raw material procurement, and production filling of fluorocarbon coatings. The products have passed environmental regulations such as ROHS and REACH. Free sample testing and on-site guidance from technical engineers are provided.
¿Por qué elegir un recubrimiento fluorocarbonado?
NúcleoVentajas
Mecanismo de resistencia a la intemperie ultrarresistente del enlace C-F
The C-F bond energy in fluorocarbon resin is 485 kJ/mol, far higher than the maximum energy of solar ultraviolet light (411 kJ/mol). Ultraviolet light cannot break the C-F chemical bond, fundamentally preventing photodegradation and yellowing of the coating. This is a molecular-level weather resistance advantage that conventional coatings (C-C bond 345 kJ/mol / C-O bond 358 kJ/mol) cannot achieve.
Validación de larga duración en exteriores de 25 años
After 25 years of outdoor natural aging tests in the Florida exposure field, the gloss retention rate of the fluorocarbon coating is >80%, with a color difference ΔE.<3。氙灯加速老化5000h（ISO 11341）Color difference ΔE<2，No Chalking、无龟裂、No Blistering。Suitable For机场、体育场、超高层Architectural等Requisitos50年vida útil de diseño的地标Artículo。
Rendimiento excepcional de autolimpieza y resistencia a la suciedad
El recubrimiento fluorocarbonado tiene una energía superficial muy baja (<23mN/m），ángulo de contacto con agua>95°. Rainwater rolls off the coating surface in spherical droplets, automatically carrying away surface dust and contaminants. After years of use, building aluminum curtain walls and metal roof panels can maintain a clean, like-new appearance, significantly reducing cleaning and maintenance costs.
Resistencia química integral
Resistant to 98% concentrated sulfuric acid / 37% hydrochloric acid / 50% sodium hydroxide / saturated brine (no change after 30 days). Resistant to wiping with organic solvents such as toluene/xylene/acetone/ethyl acetate (200 wipes without exposing the base). Resistant to industrial acidic gases such as SO₂, H₂S, and NOx. Suitable for extreme corrosive environments such as chemical plant areas and coastal high-salt fog zones.
Sistema específico para paneles de aluminio de fachadas ventiladas metálicas
Complementing the PVDF fluorocarbon roller coating system, FEVE spray-applied fluorocarbon can be cured at room temperature on-site. It is suitable for complex components such as irregular aluminum panels and steel structures that cannot undergo high-temperature baking in factories. It offers a variety of finishes, including solid colors, metallic sparkle, and pearlescent effects, with the full RAL color range available for any color selection.
Certificado conforme a normas internacionales de referencia
Compliant with AAMA 2605 (the highest performance standard of the American Architectural Manufacturers Association) and GB/T 23443-2009 (aluminum veneer for building decoration) for fluorocarbon coating standards. Passed full performance tests including ISO 16474-2 xenon arc aging, ISO 9227 salt spray, and ISO 6270 humidity resistance. Offers a 20-year warranty commitment.
TécnicoSpecifications
Parámetros básicos
Especificaciones de rendimiento
Los parámetros técnicos anteriores proceden de datos de ensayo del laboratorio de Kexin New Materials (acreditado ISO 17025); los valores reales pueden variar ligeramente según las condiciones de aplicación y el sustrato. Póngase en contacto con el soporte técnico para obtener el informe de ensayo COA más reciente.
Preguntas Frecuentes -FAQ
ApplicationProcess
Preparación del sustrato
The pre-coated epoxy or polyurethane primer and intermediate coat surfaces are fully cured. The surface is clean, free of oil, dust, and condensation. The primer and intermediate coat system must be compatible with the fluorocarbon topcoat. Ambient temperature: 5–40°C, relative humidity<80%。
Sellado con imprimación específica
Spray one coat of epoxy sealing primer specifically designed for fluorocarbon topcoat. Seal the pores on the intermediate paint surface to ensure uniform film formation of the topcoat. The primer color must coordinate with the topcoat color to avoid showing through. The topcoat can be applied after drying for 4-8 hours.
Aplicación de precisión de la capa final
Apply 2-3 coats using air spraying or HVLP spraying. The first coat should be a mist coat of 20-25μm, with a flash-off time of 20 minutes. The second coat should be a full wet coat of 30-35μm, with a flash-off time of 30 minutes. Total dry film thickness: 70-80μm. For metallic flash paint, a clear topcoat is required to protect the flash effect.
Curado ambiente / con calor
Cure at 25°C: 24 hours for dry-to-touch / 7 days for full cure. Forced drying at 60°C for 60 minutes is recommended for optimal initial performance. Strictly protect from water, moisture, and contamination during curing. At low temperatures, extend drying and curing time to 72 hours.
Acceptación de calidad estricta
After 7 days of curing, conduct a comprehensive inspection: gloss (60° angle meter), color difference (ΔE).<1.5为合格）、espesor de película、Adherencia（Pull-off method≥5MPa）、MEK擦拭（200次Sin fondo visible）。Appearance100cmVisual无Color Difference橘皮颗粒Poros (pinholing)。Provides20年Weather-Resistant质保。
AplicacionesCasos
Fachada ventilada de aluminio de terminal aeroportuaria fluorocarbonada
Recubrimiento fluorocarbonado FEVE en fachadas ventiladas de paneles de aluminio de terminales de aeropuertos internacionales: resistencia exterior 25 años, autolimpieza como nuevo.
Paneles de aluminio fluorocarbonados de edificios superaltos
Recubrimiento fluorocarbonado de fábrica en paneles decorativos de aluminio para rascacielos emblemáticos superaltos, certificado conforme al máximo estándar AAMA 2605.
Paneles metálicos de techo de estadio con recubrimiento fluorocarbonado
Aplicación a rodillo de recubrimiento fluorocarbonado en paneles metálicos de techo de grandes estadios: capa protectora exterior premium para todo clima.
Capa final fluorocarbonada para estructuras metálicas de puentes marítimos
Capa final fluorocarbonada en superficies exteriores de vigas cajón de acero de puentes marítimos: 25 años de protección en ambiente marino extremo C5-M.
Fachada ventilada de aluminio fluorocarbonada de estación de alta velocidad
Recubrimiento fluorocarbonado de fachadas ventiladas de gran superficie con paneles de aluminio en estaciones de alta velocidad, conforme a los requisitos estéticos de alta calidad de la arquitectura pública.
Capa final fluorocarbonada para plataformas marinas
Capa final fluorocarbonada en muros exteriores de la zona residencial de plataformas petrolíferas marinas: entornos adversos con UV intenso y alta niebla salina.
Recubrimiento fluorocarbonado de perfiles de aluminio para carpintería
Pulverización electrostática fluorocarbonada en perfiles de aluminio arquitectónicos para carpintería: máximo estándar de decoración y resistencia a la intemperie en materiales.
Protección fluorocarbonada para arte escultórico
Capa protectora transparente fluorocarbonada para grandes esculturas metálicas urbanas: protección artística anticorrosión permanente a la intemperie.
Capa final fluorocarbonada para tanques petrolquímicos
Fluorocarbon topcoat painting on the external walls of storage tanks in petrochemical tank farms, providing dual protection against chemical atmosphere and strong ultraviolet radiation.
Decoración metálica fluorocarbonada para recintos deportivos
Recubrimiento fluorocarbonado de paneles decorativos metálicos interiores de gran luz en recintos deportivos: estética arquitectónica de gama alta con retención permanente del color.
Capa final fluorocarbonada para barandillas de puente
Capa final fluorocarbonada de barandillas metálicas de puentes paisajísticos urbanos: perfecta unión de decoración y calidad anticorrosión.
Recubrimiento fluorocarbonado en accesos de metro
Recubrimiento fluorocarbonado de estructuras decorativas metálicas en accesos del metro: protección de alta durabilidad para instalaciones públicas urbanas.
Recubrimientos relacionadosProductos recomendados
Imprimación epoxi rica en zinc
Contenido de zinc ≥80% · Niebla salina 3000 h · Protección catódica
Más información→
Capa intermedia epoxi MIO
Una sola capa de 150 μm · Blindaje de mica de hierro · Adherencia ≥5 MPa
Más información→
Recubrimiento de fluorocarbono
25 años de resistencia climática · Autolimpiante · Sin mantenimiento
Más información→
Capa de acabado de policiloxano
Polysiloxane · UV resistant · Non-chalking
Más información→Recubrimiento de fluorocarbono·Venta directa de fábrica
Recubrimiento fluorocarbonado Kexin suministrado directamente de la fábrica de origen. Pruebas de muestras gratuitas, asistencia técnica de ingenieros en obra, calidad certificada ISO.
artículos y noticias relacionados
Para saber más: artículos técnicos y noticias del sector de Kexin New Materials