KF-EP100 electroplated silver mirror paint employs a high aspect ratio (flake aluminium powder, diameter 20-50 μm / thickness<0.1μm——径厚比>200:1) of flake aluminium pigment plus a precision orientation-alignment process to produce a plating-like chrome/silver mirror effect. Gloss >800 GU (60°), close to the 1200-1500 GU of electroplated chrome. A special sandwich build-up is used: 1) black gloss primer (mirror-reflection base); 2) silver mirror paint (aluminium flakes laid out horizontally — the single most critical step for the mirror effect, applied as a thin wet spray with tight control of the coating's rheological parameters); 3) clear topcoat (protects the delicate flake-orientation layer and adds chemical, abrasion and weather resistance). Replaces conventional electroplating — cyanide-free, no Cr(VI) emissions. Widely used for automotive interior and exterior trim parts, home-appliance panels, luxury packaging, e-cigarette housings and other high-decoration applications.
TDS Technical Data Sheet – Electroplated Silver Mirror Finish KF-EP100
Technical Data Sheet · Electroplating silver mirror paint · KF-EP100
1. Product Description
2. Typical Applications
Provides coating protection for applications in the electroplating / mirror-effect paint field. For specific uses, please contact the Kexin New Materials technical department at 400-901-0757.
3. Technical Parameters
| Product type | Two-component solventborne coating |
|---|---|
| Color | Any colour to order |
| Gloss | Semi-gloss (30-60 GU) |
| Volume solids | 50±5% |
| Recommended DFT | 30-100 μm/coat |
| Theoretical spreading rate | 5-15 m²/L |
| Mixing ratio | A:B=4:1 |
| Pot life | 4h(20°C) |
| Surface dry time (23°C) | ≤2h(23°C) |
| Hard dry time (23°C) | ≤24h(23°C) |
| Full cure | 7 days (23°C) |
| Application temperature | 5-40°C |
| Relative humidity | <85% |
| Flash point (closed cup) | approx. 25°C |
| Density (mixed) | approx. 1.4 kg/L |
| VOC content | <420 g/L |
| Adhesion | Grade 0–1 |
| Packaging Specs | 20 L drum |
| Shelf Life | 12 months(original sealed) |
| Salt spray resistance | ≥500h |
| Standard | GB/T 25263 / ISO 12944 |
4. Application Guide
Surface preparation
Thoroughly clean the substrate surface to remove oil and rust. Abrasive-blast steel to Sa2.5 (ISO 8501-1) with 40-75μm surface profile. Concrete substrate moisture content must be below 6%, grind to remove laitance. For old coatings, remove loose areas and roughen the surface.
Mixing / compounding
According to the mix ratio indicated on the product label, add the hardener (component B) slowly to the base (component A) and mechanically stir for 3-5 minutes until uniform. Let stand to mature for 10-15 minutes before use. Use up within the specified pot life after mixing.
Application method
Recommended air spray (gun orifice 1.5-2.0 mm, pressure 0.4-0.6 MPa) or airless spray (nozzle 0.38-0.53 mm, pressure 15-25 MPa). Small areas may be brushed or rolled. Keep each coat dry film thickness within the specified range.
Curing conditions
Self-cures at ambient temperature (23°C) provided relative humidity meets requirements. Do not apply under low temperature (<5°C) or high humidity (>85%). Conduct performance testing only after full cure.
5. Packaging & Storage
| Packaging Specs | 20 L drum |
|---|---|
| Storage Conditions | Store at 5–35°C in a cool, dry, ventilated place away from ignition and heat sources; keep container sealed. |
| Shelf Life | 12 months(original sealed) |
| Transport | Transport as non-hazardous goods. In summer, ship in early morning or evening; avoid sun exposure. |
6. Health & Safety Notes
⚠️ Important safety notice
Read and understand the product's MSDS (Material Safety Data Sheet) carefully before using this product.
- Proper personal protective equipment (gloves, goggles, protective suit) must be worn during application
- Ensure the work area is well ventilated
- Keep away from fire and heat sources
- Avoid inhaling vapours and mist
- Avoid contact with skin and eyes
- If you feel unwell, stop work immediately and seek medical advice
Disclaimer
The data in this TDS are typical values and do not constitute product specifications. Actual product performance may vary depending on application conditions, substrate condition and environmental factors. Users are advised to conduct small-scale sample tests before bulk use to confirm product suitability.
Kexin New Materials continually improves its products and reserves the right to modify technical parameters without prior notice. For the latest revision, visit www.psste.com/electroplating-silver-mirror-paint-tds/.