KF-IM100 inorganic zinc silicate primer is a two-component self-curing inorganic zinc-rich primer based on the hydrolytic polycondensation product of ethyl silicate (TEOS) as the film former, with a zinc dust content ≥80%. It requires moisture from the air for the hydrolytic curing reaction — at low humidity curing is slow and water misting is needed. The coating offers excellent welding/cutting performance and heat resistance up to 400°C (organic epoxy zinc-rich primers only withstand 120°C). Cathodic protection is extremely strong (zinc content higher than epoxy types), with salt spray tests reaching several thousand hours. The coating is porous (a dedicated sealer coat is required); when used with epoxy intermediate/topcoats, a mist-coat/sealing process must be applied to prevent blistering. It is the core primer for extreme corrosion environments such as offshore platforms, ships and high-temperature pipelines.
TDS Technical Data Sheet – Inorganic Zinc Silicate Primer KF-IM100
Technical Data Sheet · Inorganic zinc silicate primer · KF-IM100
1. Product Description
2. Typical Applications
Offshore oil platforms/jackets/drilling vessels (highest corrosivity class CX/Im2), ship areas above the waterline/decks/superstructures, LNG liquefied natural gas pipelines/storage tanks (withstanding alternating low temperature -196°C and high temperature 400°C), thermal power plant high-temperature pipelines/flues, steel plant/smelter high-temperature steel structures. Requires moisture-curing conditions.
3. Technical Parameters
| Product type | Two-component solvent-borne inorganic zinc silicate primer |
|---|---|
| Color | Gray |
| Gloss | Matte (<5 GU) |
| Volume solids | 45±3% |
| Recommended DFT | 50-75 μm/道 |
| Theoretical spreading rate | 6.0-9.0 m²/L |
| Mixing ratio | A:B=2:1(Weight) |
| Pot life | 4h(20°C) |
| Surface dry time (23°C) | ≤30min(23°C) |
| Hard dry time (23°C) | ≤4h(23°C) |
| Min. overcoat interval | 24h(23°C) |
| Full cure | Requires moisture curing, 24-72 h |
| Application temperature | 5-40°C |
| Relative humidity | 50-90% (moisture curing required) |
| Flash point (closed cup) | approx. 14°C (solvent-borne) |
| Density (mixed) | approx. 2.4 kg/L |
| VOC content | <600 g/L |
| Adhesion | Grade 0–1 |
| Packaging Specs | 20 L drum |
| Shelf Life | 6 months (Component B stored moisture-protected) |
| Salt spray resistance | ≥1000 h (without topcoat) |
| High-temperature resistant | 400°C(Drying) |
| Standard | ISO 12944-5 / SSPC Paint 29 |
| Product type | 2K/Two-ComponentSolvent type无机Ethyl silicateZinc-Rich Primer（湿气Curing） |
| Dry FilmZinc content | ≥80% |
| Heat resistance rating | 400°C（连续Drying） |
4. Application Guide
Surface preparation
Thoroughly clean the substrate surface, removing oil and rust. Blast steel to Sa2½ (ISO 8501-1), surface profile 40-75 μm. Concrete substrate moisture content<6%，Sanding去除浮浆。Old coating需清除松脱部分并拉毛deal with.
Mixing / compounding
According to the mix ratio indicated on the product label, add the hardener (component B) slowly to the base (component A) and mechanically stir for 3-5 minutes until uniform. Let stand to mature for 10-15 minutes before use. Use up within the specified pot life after mixing.
Application method
Recommended air spray (gun orifice 1.5-2.0 mm, pressure 0.4-0.6 MPa) or airless spray (nozzle 0.38-0.53 mm, pressure 15-25 MPa). Small areas may be brushed or rolled. Keep each coat dry film thickness within the specified range.
Curing Conditions
Self-curing at room temperature (23°C), with relative humidity meeting requirements. Low temperature (<5°C)或高湿(>Construction is prohibited under conditions of 85% (humidity). Performance testing shall be conducted after complete curing.
5. Packaging & Storage
| Packaging Specs | 20 L drum |
|---|---|
| Storage Conditions | Store at 5–35°C in a cool, dry, ventilated place away from ignition and heat sources; keep container sealed. |
| Shelf Life | 6 months (Component B stored moisture-protected) |
| Transport | Transport as non-hazardous goods. In summer, ship in early morning or evening; avoid sun exposure. |
6. Health & Safety Notes
⚠️ Important Safety Notice
Read and understand the product's MSDS (Material Safety Data Sheet) carefully before using this product.
- Proper personal protective equipment (gloves, goggles, protective suit) must be worn during application
- Ensure the work area is well ventilated
- Keep away from fire and heat sources
- Avoid inhaling vapours and mist
- Avoid contact with skin and eyes
- If you feel unwell, stop work immediately and seek medical advice
Disclaimer
The data in this TDS are typical values and do not constitute product specifications. Actual product performance may vary depending on application conditions, substrate condition and environmental factors. Users are advised to conduct small-scale sample tests before bulk use to confirm product suitability.
Kexin New Materials continuously improves its products and reserves the right to modify technical parameters without prior notice. For the latest version please visit www.psste.com/inorganic-zinc-silicate-primer-tds/ available on request.